Two-component polyurethane sealant IPS PU 2K for seams, 12 kg

Two-component polyurethane sealant of white color for seams and cracks in vertical and inclined building structures in the absence of mechanical load with permissible deformations ± 25%, bucket 12 kg

2 243,00
uah
x
компл.
=
2 243,00 uah
2243

IPS PU 2K is a two-component polyurethane construction sealant for sealing joints and cracks in vertical and inclined building structures. It can be used for sealing joints in horizontal structures in the absence of direct mechanical load. It is easily applied with a hand tool (for example, a spatula). After mixing the components, it cures as a result of a chemical reaction. The curing rate increases with increasing temperature. The sealant has excellent adhesion to most building materials, as well as good strength and deformation qualities after curing. It can be used in residential premises, provided that the sealant is fully cured before the start of operation of the premises.

Application:

• Sealing of joints and cracks in vertical and inclined building structures

• Sealing of seams and cracks in horizontal building structures in the absence of direct mechanical load

• Sealing of expansion joints with a maximum deformation of ±25 %

• Sealing of monolithic and precast reinforced concrete structures

 

Manufacturer - Tenax
Country of origin - Latvia
Number of components -Two-component
Custom specifications - Density ≈ 1,7 kg/liter
Shrinkage - 0 %
Shore hardness - A 25 ÷ 30 after 28 days, at 23 °C and relative humidity 50 %
Seam width - from 10 to 50 mm
Appearance - White thixotropic mass, other colors are possible on request
modulus of elasticity at 100 % elongation - ≤ 0.4 MPa
Elasticity - ≥ 60 % (ISO 7389)
Packaging - The bulk (component A) – in a plastic bucket, which also contains the hardener (component B) in a plastic container. It is completed in the ratio of components A: B, ready for direct mixing, namely 8.6: 1 by weight.

The total weight of the kit is 12 kg.
Operating temperature range from – 50 °C to 70 °C
Type of polymer 2-component polyurethane, cold curing after mixing the components under the influence of moisture
elongation at the moment of rupture ≥ 80 %
Conditional tensile strength - ≥ 0.4 MPa
Seam depth - from 5 to 15 mm
Pot life ≥ 5 hours (standard version), at 23 °C and 50% relative humidity ≥ 3 hours (winter version), at 23 °C and 50 % relative humidity % Decreases with increasing temperature
The warranty period of storage is 6 months in undamaged original packaging in dry warehouses at a temperature of no more than 30 °C.
Application temperature range From – 15 °C to 30 °C (standard version) – 20 °C to 10 °C (winter version)
The ratio of the width to the depth of the seam is 2:1
Permissible deformation - ± 25 %

IPS PU 2K - высококачественный двухкомпонентный полиуретановый герметик для заделки швов и трещин в вертикальных и наклонных строительных конструкциях. Может использоваться для герметизации швов в горизонтальных конструкциях при отсутствии прямой механической нагрузки. Может применяться в жилых помещениях при условии полного отверждения герметика до начала эксплуатации помещения

Преимущества:

  • Удобен в применении
  • Отличная тиксотропность, не течет в вертикальных швах
  • Хорошая адгезия к бетону, металлам и дереву
  • Устойчив к воздействию климатических факторов, УФ‑излучению
  • Сохраняет эластичность в большом диапазоне температур
  • Окрашиваемый акриловыми красками